- 密度 [g/cm3]: 1.32
- 斷裂伸長率 [%]: 123
- 彎曲強度 [MPa]: 68.7
- 彎曲模量 [MPa]: 8.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 - 1.39 g/cc | 0.0477 - 0.0502 lb/in3 | Average value: 1.35 g/cc Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 68.7 - 80.0 MPa | 9970 - 11600 psi | Average value: 75.3 MPa Grade Count:3 |
| Flexural Yield Strength | 123 - 139 MPa | 17800 - 20200 psi | Average value: 133 MPa Grade Count:3 |
| Flexural Modulus | 8.07 - 11.7 GPa | 1170 - 1700 ksi | Average value: 10.2 GPa Grade Count:3 |
| Compressive Yield Strength | 75.2 - 91.0 MPa | 10900 - 13200 psi | Average value: 81.8 MPa Grade Count:3 |
| Compressive Modulus | 12.1 - 14.7 GPa | 1750 - 2130 ksi | Average value: 13.4 GPa Grade Count:3 |