- 密度 [g/cm3]: 1.25
- 缺口沖擊強(qiáng)度: 2.67
- 斷裂伸長率 [%]: 75.0
- 彎曲強(qiáng)度 [MPa]: 35.0
- 彎曲模量 [MPa]: 6.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 - 2.00 g/cc | 0.0452 - 0.0723 lb/in3 | Average value: 1.55 g/cc Grade Count:47 |
| Apparent Bulk Density | 0.460 - 0.970 g/cc | 0.0166 - 0.0350 lb/in3 | Average value: 0.681 g/cc Grade Count:43 |
| Linear Mold Shrinkage | -0.000300 - 0.00950 cm/cm | -0.000300 - 0.00950 in/in | Average value: 0.00422 cm/cm Grade Count:46 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 250 - 500 MPa | 36300 - 72500 psi | Average value: 337 MPa Grade Count:28 |
| Tensile Strength, Ultimate | 35.0 - 227 MPa | 5080 - 32900 psi | Average value: 64.1 MPa Grade Count:21 |
| Modulus of Elasticity | 6.50 - 13.5 GPa | 943 - 1960 ksi | Average value: 9.05 GPa Grade Count:19 |
| Flexural Yield Strength | 75.0 - 358 MPa | 10900 - 51900 psi | Average value: 110 MPa Grade Count:47 |
| Flexural Modulus | 6.50 - 25.0 GPa | 943 - 3630 ksi | Average value: 9.99 GPa Grade Count:46 |
| Compressive Yield Strength | 135 - 250 MPa | 19600 - 36300 psi | Average value: 216 MPa Grade Count:24 |
| Izod Impact, Notched | 2.67 - 6.40 J/cm | 5.00 - 12.0 ft-lb/in | Average value: 4.55 J/cm Grade Count:3 |
| Charpy Impact Unnotched | 0.300 - 1.50 J/cm2 | 1.43 - 7.14 ft-lb/in2 | Average value: 0.718 J/cm2 Grade Count:44 |
| Charpy Impact, Notched | 0.130 - 0.850 J/cm2 | 0.619 - 4.05 ft-lb/in2 | Average value: 0.218 J/cm2 Grade Count:42 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+7 - 1.00e+12 ohm-cm | 1.00e+7 - 1.00e+12 ohm-cm | Average value: 5.12e+11 ohm-cm Grade Count:41 |
| Surface Resistance | 1.00e+6 - 1.00e+11 ohm | 1.00e+6 - 1.00e+11 ohm | Average value: 5.12e+10 ohm Grade Count:41 |
| Dielectric Constant | 5.00 - 20.0 | 5.00 - 20.0 | Average value: 10.0 Grade Count:39 |
| Dielectric Strength | 5.00 - 35.0 kV/mm | 127 - 889 kV/in | Average value: 22.5 kV/mm Grade Count:34 |
| Dissipation Factor | 0.0100 - 0.400 | 0.0100 - 0.400 | Average value: 0.205 Grade Count:40 |
| Arc Resistance | 60.0 - 240 sec | 60.0 - 240 sec | Average value: 132 sec Grade Count:16 |
| High Voltage Arc Resistance to Ignition (HVAR) | 300 sec | 300 sec | Average value: 300 sec Grade Count:5 |
| Comparative Tracking Index | 100 - 250 V | 100 - 250 V | Average value: 152 V Grade Count:26 |
| Hot Wire Ignition, HWI | 30.0 - 120 sec | 30.0 - 120 sec | Average value: 108 sec Grade Count:14 |
| High Amp Arc Ignition, HAI | 0.000 - 120 arcs | 0.000 - 120 arcs | Average value: 70.6 arcs Grade Count:14 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 150 mm/min | 0.000 - 5.91 in/min | Average value: 19.8 mm/min Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 130 - 280 °C | 266 - 536 °F | Average value: 179 °C Grade Count:27 |
| Deflection Temperature at 8.0 MPa | 105 - 190 °C | 221 - 374 °F | Average value: 134 °C Grade Count:44 |
| UL RTI, Electrical | 150 °C | 302 °F | Average value: 150 °C Grade Count:15 |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:15 |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | Average value: 150 °C Grade Count:15 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:17 |
| Shrinkage | 0.000 - 1.00 % | 0.000 - 1.00 % | Average value: 0.337 % Grade Count:45 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 60.0 - 75.0 °C | 140 - 167 °F | Average value: 67.5 °C Grade Count:44 |
| Nozzle Temperature | 80.0 - 100 °C | 176 - 212 °F | Average value: 90.0 °C Grade Count:44 |
| Melt Temperature | 80.0 - 100 °C | 176 - 212 °F | Average value: 90.0 °C Grade Count:44 |
| Mold Temperature | 160 - 190 °C | 320 - 374 °F | Average value: 175 °C Grade Count:44 |
| Injection Pressure | 15.0 MPa | 2180 psi | Average value: 15.0 MPa Grade Count:44 |
| Back Pressure | 0.500 - 2.00 MPa | 72.5 - 290 psi | Average value: 1.25 MPa Grade Count:44 |
| Cure Time | 0.167 - 0.667 min | 0.00278 - 0.0111 hour | Average value: 0.375 min Grade Count:44 |
| Shelf Life | 2.00 - 6.00 Month @Temperature -17.8 - 4.44 °C | 2.00 - 6.00 Month @Temperature 0.000 - 40.0 °F | Average value: 4.00 Month Grade Count:2 |