- 密度 [g/cm3]: 1.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 74 | 74 | Silicone Property; Arlon SQA-TMS-014 | ||
| Tensile Strength | 5.79 MPa | 840 psi | Silicone Property; Arlon SQA-TMS-008 | ||
| Elongation at Break | 130 % | 130 % | Silicone Property; Arlon SQA-TMS-008 | ||
| Tear Strength | 15.8 kN/m | 90.0 pli | Silicone Property; Arlon SQA-TMS-029 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Arlon SQA-TMS-020 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | File E54153; 15 mil to 30 mil thickness on a substrate or carrier | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||