| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 267 microns | 10.5 mil | Rubber | ||
| 381 microns | 15.0 mil | Substrate | |||
| 635 microns | 25.0 mil | Overall thickness | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property | ||
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Silicone Property | ||
| Elongation at Break | >= 300 % | >= 300 % | Silicone Property | ||
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 3.0 | 3.0 | Char Length, inches; FTMS 191A; Method 5903 | ||
| 25 | 25 | Flame and Glow Time, seconds; FTMS 191A; Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 32 | ||||
| Uncoated Fabric Break Strength (lb/in) | 350 | Fill Direction | |||
| 400 | Warp Direction | ||||