- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.19
- 缺口沖擊強(qiáng)度: 5.5
- 彎曲強(qiáng)度 [MPa]: 22.8
- 彎曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in3 | ASTM D792 |
| Water Absorption | 0.19 % | 0.19 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 22.8 MPa | 3310 psi | ASTM D638 |
| Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 10.8 kV/mm | 274 kV/in | Short Time; ASTM D149 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | 5VA | 5VA | 0.062 inch thickness |