- 密度 [g/cm3]: 1.82
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 5.1
- 彎曲強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in3 | |
| Water Absorption | 0.10 % | 0.10 % | in 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 29 - 35 | 29 - 35 | ASTM D2583 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Compressive Strength | 165 MPa | 23900 psi | ASTM D695 |
| Izod Impact, Notched | 5.10 J/cm | 9.55 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.8 kV/mm | 401 kV/in | ASTM D149 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |