- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.45
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.79 g/cc | 1.79 g/cc | |
| Water Absorption | 0.10 % | 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00030 cm/cm | 0.00030 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa @Temperature 150 °C | 725 ksi @Temperature 302 °F | Secant, 0.5 mm; ASTM D790 |
| 10.0 GPa @Temperature 23.0 °C | 1450 ksi @Temperature 73.4 °F | Secant, 0.5 mm; ASTM D790 | |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.20 GPa | 609 ksi | Calculated |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 μm/m-°C | 13.9 μin/in-°F | XY Direction |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | |
| Flame Spread Index | <= 35 | <= 35 | ASTM E162 |
| NBS Smoke Density | <= 25 | <= 25 | Ds @ 4 minutes; ASTM E662 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Injection Molding |
| Clamp Pressure | <= 6.89 MPa | <= 1000 psi | Molding Pressure |