- 缺口沖擊強度: 7.47
- 彎曲強度 [MPa]: 68.9
- 彎曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00020 cm/cm | 0.00020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | tangent; ASTM D638 |
| Flexural Strength | 169 MPa | 24500 psi | ASTM D790-1 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | Tangent; ASTM D790-1 |
| Poissons Ratio | 0.30 | 0.30 | |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.61 J/cm | 18.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 μm/m-°C @Temperature 20.0 °C | 20.0 μin/in-°F @Temperature 68.0 °F | Z-direction |
| CTE, linear, Transverse to Flow | 27.0 μm/m-°C @Temperature 20.0 °C | 15.0 μin/in-°F @Temperature 68.0 °F | XY-direction |
| Specific Heat Capacity | 0.335 J/g-°C | 0.0800 BTU/lb-°F | |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft2-°F | |