- 密度 [g/cm3]: 2.0
- 吸水率 [%]: 0.5
- 缺口沖擊強(qiáng)度: 10.4
- 彎曲強(qiáng)度 [MPa]: 160.0
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in3 | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 68 | 68 | |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Modulus of Elasticity | 15.7 GPa | 2280 ksi | ASTM D638 |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Compressive Strength | 220 MPa | 31900 psi | ASTM D695 |
| Izod Impact, Notched | 10.4 J/cm | 19.5 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.4 @Frequency 60 Hz | 4.4 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 188 sec | 188 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.9 μm/m-°C @Temperature 20.0 °C | 9.40 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.26 J/g-°C | 0.300 BTU/lb-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 5V |