- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 4.4
- 彎曲強度 [MPa]: 37.0
- 彎曲模量 [MPa]: 9.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 68 | 68 | |
| Tensile Strength, Ultimate | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 0.40 % | 0.40 % | ASTM D638 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Compressive Strength | 160 MPa | 23200 psi | ASTM D695 |
| Izod Impact, Notched | 4.40 J/cm | 8.24 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.4 @Frequency 60 Hz | 4.4 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 188 sec | 188 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.26 J/g-°C | 0.300 BTU/lb-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 5V |