- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 6.4
- 彎曲強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in3 | ASTM D572 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 52 | 52 | |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | |
| Flexural Strength | 172 MPa | 24900 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Compressive Strength | 228 MPa | 33100 psi | |
| Shear Strength | 97.0 MPa | 14100 psi | ASTM D732 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | edgewise; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.2 @Frequency 60 Hz | 4.2 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 1.59 mm | 483 kV/in @Thickness 0.0625 in | Perpendicular, Short Time in Oil and Air; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 60 Hz | 0.010 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | >= 500 V | >= 500 V | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 220 °C | 428 °F | Approximate temperature class |
| Flammability, UL94 | HB | HB | File No.E81893 |