- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 4.5
- 彎曲強度 [MPa]: 76.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in3 | ASTM D572 |
| Water Absorption | 0.35 % | 0.35 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 48 | 48 | |
| Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | |
| Flexural Strength | 172 MPa | 24900 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Compressive Strength | 276 MPa | 40000 psi | |
| Shear Strength | 103 MPa | 14900 psi | ASTM D732 |
| Izod Impact, Notched | 4.50 J/cm | 8.43 ft-lb/in | edgewise; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.8 @Frequency 60 Hz | 4.8 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.59 mm | 508 kV/in @Thickness 0.0625 in | Perpendicular, Short Time in Oil; ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 60 Hz | 0.020 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 155 °C | 311 °F | Approximate temperature class |