- 密度 [g/cm3]: 1.7
- 缺口沖擊強度: 8.5
- 斷裂伸長率 [%]: 190
- 彎曲強度 [MPa]: 75.0
- 彎曲模量 [MPa]: 9.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in3 | |
| Water Absorption | <= 0.35 % | <= 0.35 % | ASTM D570-63 |
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 55 - 65 | 55 - 65 | ASTM D2583 |
| Tensile Strength, Ultimate | 75.0 - 105 MPa | 10900 - 15200 psi | ASTM D638-68 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790-70 |
| Flexural Modulus | 9.70 - 12.4 GPa | 1410 - 1800 ksi | ASTM D790-70 |
| Izod Impact, Notched | 8.50 J/cm | 15.9 ft-lb/in | ASTM D256-70 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 17.5 μm/m-°C @Temperature 23.0 - 150 °C | 9.72 μin/in-°F @Temperature 73.4 - 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 235 °C | >= 455 °F | ASTM D648-61 |