- 吸水率 [%]: 0.2
- 彎曲強(qiáng)度 [MPa]: 86.2
- 彎曲模量 [MPa]: 6.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.00026 cm/cm | 0.00026 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ISO 62 |
| 58.6 MPa @Temperature 150 °C | 8500 psi @Temperature 302 °F | ISO 62 | |
| Tensile Modulus | 15.2 GPa | 2200 ksi | tangent; ISO 527 |
| 8.27 GPa @Temperature 150 °C | 1200 ksi @Temperature 302 °F | ISO 527 | |
| Flexural Strength | 176 MPa | 25500 psi | ISO 178 |
| 121 MPa @Temperature 150 °C | 17500 psi @Temperature 302 °F | ISO 178 | |
| Flexural Modulus | 6.21 GPa @Thickness 2.50 mm, Temperature 150 °C | 900 ksi @Thickness 0.0984 in, Temperature 302 °F | Secant; ISO 178 |
| 8.27 GPa @Thickness 2.50 mm, Temperature 22.0 °C | 1200 ksi @Thickness 0.0984 in, Temperature 71.6 °F | Secant; ISO 178 | |
| 8.27 GPa @Thickness 0.500 mm, Temperature 150 °C | 1200 ksi @Thickness 0.0197 in, Temperature 302 °F | Secant; ISO 178 | |
| 11.7 GPa @Thickness 0.500 mm, Temperature 22.0 °C | 1700 ksi @Thickness 0.0197 in, Temperature 71.6 °F | Secant; ISO 178 | |
| Izod Impact, Unnotched | 12.8 J/cm | 24.0 ft-lb/in | ASTM D4812 |
| Impact | 0.23 | 0.23 | (in) High Speed Impact (Deflection Max Load); ISO 6603-2 |
| 517 | 517 | (lb) High Speed Impact (Impact Max Load); ISO 6603-2 | |
| Impact Test | 6.91 J | 5.10 ft-lb | High Speed Impact (Energy Max Load); ISO 6603-2 |
| 12.6 J | 9.30 ft-lb | High Speed Impact (Total Energy); ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 27.0 μm/m-°C @Temperature 20.0 °C | 15.0 μin/in-°F @Temperature 68.0 °F | Z-direction; ASTM D696 |
| CTE, linear, Transverse to Flow | 18.0 μm/m-°C @Temperature 20.0 °C | 10.0 μin/in-°F @Temperature 68.0 °F | XY-direction; ASTM D696 |
| Thermal Conductivity | 0.550 W/m-K | 3.82 BTU-in/hr-ft2-°F | ASTM 1530-93 |
| Glass Transition Temp, Tg | 188 °C | 370 °F | ISO 6721 DMS |