- 吸水率 [%]: 0.08
- 缺口沖擊強(qiáng)度: 17.6
- 彎曲模量 [MPa]: 20.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.87 g/cc | 1.87 g/cc | ASTM D792 | ||
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 68 | 68 | ASTM D2583 | ||
| Tensile Strength | 344 MPa | 49900 psi | ASTM D638 | ||
| Tensile Modulus | 26.1 GPa | 3790 ksi | ASTM D638 | ||
| Flexural Strength | 585 MPa | 84800 psi | ASTM D790 | ||
| Flexural Modulus | 20.6 GPa | 2990 ksi | ASTM D790 | ||
| Poissons Ratio | 0.38 | 0.38 | ASTM D638 | ||
| Izod Impact, Notched | 17.6 J/cm | 33.0 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 125 °C | 257 °F | DMA | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 132 - 149 °C @Thickness 12.7 mm | 270 - 300 °F @Thickness 0.500 in | Compression Molding | ||
| Clamp Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |||
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C | 0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F | |||
| Shelf Life | 2.00 Month @Temperature 23.9 °C | 2.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Fiber Length (in) | 1 | Glass, nominal | |||