- 斷裂伸長率 [%]: 38.0
- 彎曲模量 [MPa]: 10.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.060 % @Temperature 23.0 °C, Time 86400 sec | <= 0.060 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASM D638 | ||
| Tensile Modulus | 9.50 GPa | 1380 ksi | ASTM D638 | ||
| Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 | ||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 0.0143 ohm-cm | 0.0143 ohm-cm | In Plane (X,Y direction) | ||
| 0.03125 ohm-cm | 0.03125 ohm-cm | Through Plane (Z direction) | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 0.846 J/g-°C | 0.202 BTU/lb-°F | E1461-92 | ||
| Thermal Conductivity | 13.4 W/m-K | 93.0 BTU-in/hr-ft2-°F | |||
| Glass Transition Temp, Tg | 189 °C | 372 °F | |||
| Flammability, UL94 | V-0 @Thickness 3.56 mm | V-0 @Thickness 0.140 in | |||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 149 - 160 °C | 300 - 320 °F | |||
| Cure Time | 0.500 - 1.00 min | 0.00833 - 0.0167 hour | |||
| Descriptive Properties | |||||
| Diffusivity | 0.0889 cm2/s | ||||
| DMA-Modulus | 13.8 | @ 25°C, ASTM D4065 | |||
| 3.1 | @ 200°C, ASTM D4065 | ||||
| 5.4 | @ 175°C, ASTM D4065 | ||||
| 6.8 | @ 150°C, ASTM D4065 | ||||
| 9.6 | @ 100°C, ASTM D4065 | ||||
| Flowability | 270 cm2 | ||||
| Post bake, 350°F | 15 mins | after reaching 350°f | |||
| Press Close Speed | <2 sec | after material begins flowing | |||
| Recommended tonnage | >40 Mpa | on projected part area | |||