- 密度 [g/cm3]: 1.5
- 彎曲模量 [MPa]: 5.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.700 g/cc | 0.0217 - 0.0253 lb/in3 | DIN 53 468 | ||
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | DIN 53 464 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 178 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 178 | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 | ||
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 | ||
| Flexural Modulus | 5.50 - 6.50 GPa | 798 - 943 ksi | ISO 178 | ||
| Compressive Strength | 210 - 240 MPa | 30500 - 34800 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.60 - 1.80 J/cm2 | 7.61 - 8.57 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | DIN 53 483 | ||
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | DIN 53 482 | ||
| Dielectric Constant | 6.0 - 7.0 | 6.0 - 7.0 | DIN 53 483 | ||
| Dissipation Factor | 0.050 @Frequency 1000 Hz | 0.050 @Frequency 1000 Hz | tan delta; DIN 53 483 | ||
| Arc Resistance | >= 120 sec | >= 120 sec | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.258 W/m-K | 1.79 BTU-in/hr-ft2-°F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 175 | ||
| Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 175 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 30 % | >= 30 % | ASTM D2863 | ||
| Shrinkage | 1.3 - 1.6 % | 1.3 - 1.6 % | Post Shrinkage, 110°C, 7 days; DIN 53 464 | ||
| Descriptive Properties | |||||
| Glow Bar 960°C 180 sec | BH2-8 | IEC 707 | |||
| Water Absorption [mg] | <200 | DIN 53 495/23°C 96h | |||