| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | DIN 53 464 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | >= 45.0 MPa | >= 6530 psi | ISO 178 | ||
| Flexural Strength | >= 80.0 MPa | >= 11600 psi | ISO 178 | ||
| Charpy Impact Unnotched | >= 0.500 J/cm2 | >= 2.38 ft-lb/in2 | 1eU; ISO 179 | ||
| Charpy Impact, Notched | >= 0.110 J/cm2 | >= 0.524 ft-lb/in2 | 1eU; ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | DIN 53 482 | ||
| Dielectric Constant | 5.0 | 5.0 | DIN 53 483 | ||
| Comparative Tracking Index | >= 500 V | >= 500 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 155 °C | >= 311 °F | ISO 175 | ||
| Deflection Temperature at 8.0 MPa | >= 110 °C | >= 230 °F | ISO 175 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 40 % | >= 40 % | ASTM D2863 | ||
| Shrinkage | 1.5 - 1.8 % | 1.5 - 1.8 % | Post Shrinkage; DIN 53 464 | ||
| Descriptive Properties | |||||
| Acetic Acid Fa Emission | >3 mg/l | DIN 7708 | |||
| Ethanol Fa Emission | >3 mg/l | DIN 7708 | |||
| Glow Bar 960°C 180 sec | passes | IEC 707 | |||
| H2O Fa Emission | >3 mg/l | DIN 7708 | |||
| Water Absorption [mg] | <200 | DIN 53 495/23°C 96h | |||