| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 43.5 MPa | 6310 psi | |||
| Elongation at Break | 8.0 % | 8.0 % | |||
| Tensile Modulus | 2.28 GPa | 331 ksi | |||
| Compressive Strength | 62.1 MPa | 9010 psi | |||
| Compressive Modulus | 1.80 GPa | 261 ksi | |||
| Adhesive Bond Strength | 3.50 MPa @Temperature 93.0 °C | 508 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 29.0 MPa @Temperature -55.0 °C | 4210 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 31.0 MPa @Temperature 25.0 °C | 4500 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Peel Strength | 9.00 kN/m | 51.4 pli | Bell Peel | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 49.0 °C | 120 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 82.0 °C | 1.00 hour @Temperature 180 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 60 min | 60 min | |||
| Descriptive Properties | |||||
| Consistency | Low Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:25 | ||||
| Peel Strength | High | ||||