- 密度 [g/cm3]: 1.51
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in3 | ASTM D1475 | ||
| Water Absorption | <= 0.20 % | <= 0.20 % | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 | 90 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 49.6 MPa | 7200 psi | Cast bar; ASTM D638 | ||
| Elongation at Break | 6.0 % | 6.0 % | ASTM D412 | ||
| Compressive Yield Strength | 98.6 MPa | 14300 psi | ASTM D695 | ||
| Adhesive Bond Strength | 24.0 MPa | 3480 psi | Lap Shear; Aluminum to Aluminum; ASTM D1002 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 45.0 - 60.0 min | 0.750 - 1.00 hour | Full cure in 45 to 60 mins at 140°F. | ||
| 180 - 240 min | 3.00 - 4.00 hour | Handling strength in 3 to 4 hrs. | |||
| 360 - 480 min | 6.00 - 8.00 hour | Full cure in 6 to 8 hours at 77°F. | |||
| Gel Time | 20.0 - 30.0 min | 20.0 - 30.0 min | Value for 1 lbm; ASTM D2471 | ||
| Descriptive Properties | |||||
| Mix Ratio | 1:1 | Resin:Hardener by Volume | |||
| 100:100 | Resin:Hardener by Weight | ||||