- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.278
- 拉伸強度 [MPa]: 56.0
- 彎曲模量 [MPa]: 2.423
- 熱變形溫度 [℃]: 59.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc @Temperature 25.0 °C | 0.0408 lb/in3 @Temperature 77.0 °F | |||
| Viscosity | 700 cP @Temperature 30.0 °C | 700 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | ASTM D2240 | ||
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ASTM D638M | ||
| Elongation at Break | 5.4 - 7.1 % | 5.4 - 7.1 % | ASTM D638M | ||
| Modulus of Elasticity | 2.117 GPa | 307.0 ksi | ASTM D638M | ||
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790M | ||
| Flexural Modulus | 2.423 GPa | 351.4 ksi | ASTM D790M | ||
| Izod Impact, Notched | 0.278 J/cm | 0.521 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 - 72.0 °C | 138 - 162 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Transparent Amber | ||||
| Dp (mm) | 0.14 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 51 | Exposure that gives 0.254mm thickness | |||
| E5 (mJ/cm2) | 20 | Exposure that gives 0.127mm thickness | |||
| Ec (mJ/cm2) | 8.2 | Critical exposure | |||