- 密度 [g/cm3]: 1.11
- 缺口沖擊強(qiáng)度: 0.59
- 拉伸強(qiáng)度 [MPa]: 26.0
- 彎曲模量 [MPa]: 0.690
- 熱變形溫度 [℃]: 54.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc @Temperature 25.0 °C | 0.0401 lb/in3 @Temperature 77.0 °F | |||
| Viscosity | 600 cP @Temperature 30.0 °C | 600 cP @Temperature 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 76 | 76 | ASTM D2240 | ||
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638M | ||
| Elongation at Break | 27 % | 27 % | ASTM D638M | ||
| Modulus of Elasticity | 0.276 - 0.703 GPa | 40.0 - 102 ksi | ASTM D638M | ||
| Flexural Strength | 26.0 MPa | 3770 psi | ASTM D790M | ||
| Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790M | ||
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256A | ||
| Tear Strength, Total | 205 N | 46.1 lb (f) | Graves; ASTM D1004 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Transparent Amber | ||||
| Dp (mm) | 0.157 | Slope of cure-depth vs. ln(E) curve | |||
| E10 (mJ/cm2) | 35 | Exposure that gives 0.254mm thickness | |||
| E5 (mJ/cm2) | 15 | Exposure that gives 0.127mm thickness | |||
| Ec (mJ/cm2) | 6.75 | Critical exposure | |||