- 密度 [g/cm3]: 1.9
- 彎曲強(qiáng)度 [MPa]: 68.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in3 | |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | |
| Viscosity | 25000 cP | 25000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | |
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 64.0 μm/m-°C @Temperature 20.0 °C | 35.6 μin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 1.87 W/m-K | 13.0 BTU-in/hr-ft2-°F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Shrinkage | 0.20 % | 0.20 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | at 250°F |