- 彎曲強度 [MPa]: 248.0
- 彎曲模量 [MPa]: 17.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | |
| Filler Content | 64 % | 64 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 70 | 70 | |
| Tensile Strength, Ultimate | 248 MPa | 36000 psi | 45° stress angle |
| 248 MPa | 36000 psi | 90° stress angle | |
| 331 MPa | 48000 psi | 0° stress angle | |
| Tensile Modulus | 17.2 GPa | 2500 ksi | 0° stress angle |
| 19.3 GPa | 2800 ksi | 45° stress angle | |
| 19.3 GPa | 2800 ksi | 90° stress angle | |
| Flexural Strength | 483 MPa | 70000 psi | 45° stress angle |
| 517 MPa | 75000 psi | 90° stress angle | |
| 524 MPa | 76000 psi | 0° stress angle | |
| Flexural Modulus | 17.9 GPa | 2600 ksi | 90° stress angle |
| 18.6 GPa | 2700 ksi | 45° stress angle | |
| 20.0 GPa | 2900 ksi | 0° stress angle | |
| Compressive Strength | 441 MPa | 64000 psi | 45° stress angle |
| 441 MPa | 64000 psi | 90° stress angle | |
| 517 MPa | 75000 psi | 0° stress angle | |
| Fatigue Strength | 110 MPa @# of Cycles 1.00e+8 | 16000 psi @# of Cycles 1.00e+8 | Flexural Fatigue (SN) |
| 131 MPa @# of Cycles 1.00e+7 | 19000 psi @# of Cycles 1.00e+7 | Flexural Fatigue (SN) | |
| 165 MPa @# of Cycles 1.00e+6 | 24000 psi @# of Cycles 1.00e+6 | Flexural Fatigue (SN) | |
| 193 MPa @# of Cycles 100000 | 28000 psi @# of Cycles 100000 | Flexural Fatigue (SN) | |
| 234 MPa @# of Cycles 10000 | 34000 psi @# of Cycles 10000 | Flexural Fatigue (SN) | |
| 276 MPa @# of Cycles 3000 | 40000 psi @# of Cycles 3000 | Flexural Fatigue (SN) | |
| Shear Modulus | 65.5 GPa | 9500 ksi | Short Beam; 0° stress angle; span/depth 5:1; ASTM D2344-76; span/depth 5:1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.90e+17 ohm-cm | 4.90e+17 ohm-cm | 50% RH and at 90% RH |
| Insulation Resistance | 5.30e+15 ohm | 5.30e+15 ohm | 50% RH |
| 6.80e+10 ohm @Temperature 150 °C | 6.80e+10 ohm @Temperature 302 °F | 50% RH | |
| 6.20e+11 ohm @Temperature 120 °C | 6.20e+11 ohm @Temperature 248 °F | 50% RH | |
| 9.70e+12 ohm @Temperature 60.0 °C | 9.70e+12 ohm @Temperature 140 °F | 90% RH | |
| 2.70e+14 ohm @Temperature 60.0 °C | 2.70e+14 ohm @Temperature 140 °F | 50% RH | |
| 3.30e+14 ohm @Temperature 23.0 °C | 3.30e+14 ohm @Temperature 73.4 °F | 90% RH | |
| Dielectric Constant | 4.8 @Frequency 1e+6 Hz | 4.8 @Frequency 1e+6 Hz | 50% RH |
| 5.2 @Frequency 1000 Hz | 5.2 @Frequency 1000 Hz | 50% RH | |
| 4.4 @Frequency 3.00e+7 Hz, Temperature 23.0 °C | 4.4 @Frequency 3.00e+7 Hz, Temperature 73.4 °F | 50% RH | |
| 5.1 @Frequency 100000 Hz, Temperature 23.0 °C | 5.1 @Frequency 100000 Hz, Temperature 73.4 °F | 50% RH | |
| 5.3 @Frequency 60.0 Hz, Temperature 23.0 °C | 5.3 @Frequency 60.0 Hz, Temperature 73.4 °F | 50% RH | |
| 5.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 5.5 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 90% RH | |
| 5.7 @Frequency 1000 Hz, Temperature 60.0 °C | 5.7 @Frequency 1000 Hz, Temperature 140 °F | 50% RH | |
| 6.1 @Frequency 1000 Hz, Temperature 120 °C | 6.1 @Frequency 1000 Hz, Temperature 248 °F | 50% RH | |
| 6.5 @Frequency 1000 Hz, Temperature 23.0 °C | 6.5 @Frequency 1000 Hz, Temperature 73.4 °F | 90% RH | |
| 6.8 @Frequency 1000 Hz, Temperature 60.0 °C | 6.8 @Frequency 1000 Hz, Temperature 140 °F | 90% RH | |
| 7.0 @Frequency 60.0 Hz, Temperature 23.0 °C | 7.0 @Frequency 60.0 Hz, Temperature 73.4 °F | 90% RH | |
| 7.3 @Frequency 1000 Hz, Temperature 150 °C | 7.3 @Frequency 1000 Hz, Temperature 302 °F | 50% RH | |
| Dielectric Strength | 24.4 kV/mm | 620 kV/in | 50% RH |
| Dissipation Factor | 0.0060 @Frequency 1000 Hz | 0.0060 @Frequency 1000 Hz | 50% RH |
| 0.017 @Frequency 1e+6 Hz | 0.017 @Frequency 1e+6 Hz | 50% RH | |
| 0.0033 @Frequency 1000 Hz, Temperature 120 °C | 0.0033 @Frequency 1000 Hz, Temperature 248 °F | 50% RH | |
| 0.0052 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.0052 @Frequency 60.0 Hz, Temperature 73.4 °F | 50% RH | |
| 0.0087 @Frequency 1000 Hz, Temperature 60.0 °C | 0.0087 @Frequency 1000 Hz, Temperature 140 °F | 50% RH | |
| 0.014 @Frequency 100000 Hz, Temperature 23.0 °C | 0.014 @Frequency 100000 Hz, Temperature 73.4 °F | 50% RH | |
| 0.019 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.019 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 90% RH | |
| 0.023 @Frequency 3.00e+7 Hz, Temperature 23.0 °C | 0.023 @Frequency 3.00e+7 Hz, Temperature 73.4 °F | 50% RH | |
| 0.036 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.036 @Frequency 60.0 Hz, Temperature 73.4 °F | 90% RH | |
| 0.050 @Frequency 1000 Hz, Temperature 23.0 °C | 0.050 @Frequency 1000 Hz, Temperature 73.4 °F | 90% RH | |
| 0.054 @Frequency 1000 Hz, Temperature 60.0 °C | 0.054 @Frequency 1000 Hz, Temperature 140 °F | 90% RH | |
| 0.13 @Frequency 1000 Hz, Temperature 150 °C | 0.13 @Frequency 1000 Hz, Temperature 302 °F | 50% RH | |
| Arc Resistance | 20 sec | 20 sec | with filaments; 50% RH and at 90% RH |
| 80 sec | 80 sec | across filaments; 50% RH and at 90% RH | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.1 μm/m-°C @Temperature -34.4 - 93.3 °C | 8.40 μin/in-°F @Temperature -30.0 - 200 °F | parallel to one array of filaments; ASTM D696-42T |
| Specific Heat Capacity | 0.879 J/g-°C | 0.210 BTU/lb-°F | |
| Thermal Conductivity | 0.334 W/m-K @Temperature 7.22 °C | 2.32 BTU-in/hr-ft2-°F @Temperature 45.0 °F | on 1 inch thick isotropic laminate |
| 0.336 W/m-K @Temperature 2.22 °C | 2.33 BTU-in/hr-ft2-°F @Temperature 36.0 °F | on 1 inch thick isotropic laminate | |
| 0.342 W/m-K @Temperature 51.7 °C | 2.37 BTU-in/hr-ft2-°F @Temperature 125 °F | on 1 inch thick isotropic laminate | |
| 0.346 W/m-K @Temperature 85.6 °C | 2.40 BTU-in/hr-ft2-°F @Temperature 186 °F | on 1 inch thick isotropic laminate | |