- 密度 [g/cm3]: 1.86
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.16
- 彎曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D1895 | ||
| Density | 1.86 g/cc | 0.0672 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.30 % @Temperature 50.0 °C, Time 173000 sec | 0.30 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0035 - 0.0050 cm/cm | 0.0035 - 0.0050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D638 | ||
| Flexural Strength | 94.0 MPa | 13600 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 | ||
| Compressive Strength | 213 MPa | 30900 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 13.8 kV/mm @Frequency 60.0 Hz | 351 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 16.0 kV/mm @Frequency 60.0 Hz | 406 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 178 sec | 178 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Transfer | |||||