- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.01
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Oxygen Permeability | 970 cm3 mil/(m2 day atm) | 62.6 cm3 mil/(100 in2 day atm) | |||
| Water Vapor Permeability | 3.70 g mil/ (m2 day) | 0.239 g mil/ (100 in2 day) | |||
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 | ||
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C | 0.010 % @Temperature 73.4 °F | ISO 62 | ||
| Thickness | 70.0 microns | 2.76 mil | Film | ||
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| 10.1 g/10 min @Load 2.16 kg, Temperature 230 °C | 10.1 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 3.4 % | 3.4 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 3.4 % | 3.4 % | ISO 527-3 | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | Film, TD; ISO 527-3 | ||
| 2.10 GPa | 305 ksi | Film, MD; ISO 527-3 | |||
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 50.0 MPa | 7250 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 78.0 °C | 172 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Descriptive Properties | |||||
| Type of film extrusion | Cast | Test specimen | |||