- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.01
- 缺口沖擊強度: 0.6
- 彎曲模量 [MPa]: 2.10
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | ASTM D792 |
| Water Absorption | <= 0.010 % | <= 0.010 % | ASTM D570 |
| Moisture Vapor Transmission | 0.0900 cc-mm/m2-24hr-atm | 0.229 cc-mil/100 in2-24hr-atm | 40°C, 90%, 50-300μm; JIS K7129 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 280 °C | 20 g/10 min @Load 4.76 lb, Temperature 536 °F | JIS K 6719 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 20 | 20 | ASTM D785 |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| Elongation at Break | 90 % | 90 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC250 |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz | 2.3 @Frequency 1e+6 Hz | IEC250 |
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | ASTM D149 |
| Dissipation Factor | 0.00020 @Frequency 1e+6 Hz | 0.00020 @Frequency 1e+6 Hz | IEC250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ASTM D648 |
| Glass Transition Temp, Tg | 102 °C | 216 °F | JIS K7121 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % @Thickness 3.00 mm | 92 % @Thickness 0.118 in | ASTM D1003 |