- 密度 [g/cm3]: 1.17
- 缺口沖擊強度: 0.32
- 彎曲模量 [MPa]: 16.68
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| Tensile Modulus | 16.04 GPa | 2326 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 16.68 GPa | 2419 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 - 100000 ohm | 10 - 100000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 2.80 μm/m-°C @Temperature -40.0 - 40.0 °C | 1.56 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 12.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 7.00 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C @Thickness 3.20 mm | 302 °F @Thickness 0.126 in | unannealed; ASTM D648 |