- 熔體流動速率 [g/10min]: 26.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.01
- 彎曲強度 [MPa]: 46.0
- 熱變形溫度 [℃]: 130.0
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.010 % | 0.010 % | immersion @23°C; ISO 62 | ||
| Water Absorption at Saturation | 0.010 % | 0.010 % | |||
| Water Vapor Transmission | 0.0300 g/m2/day | 0.00193 g/100 in2/day | [g·mm/m2·d] @ 23°C and 85% RH; DIN 53122 | ||
| 0.250 g/m2/day | 0.0161 g/100 in2/day | Good barrier properties | |||
| Melt Flow | 26 g/10 min @Load 2.16 kg, Temperature 245 °C | 26 g/10 min @Load 4.76 lb, Temperature 473 °F | ISO 1133 | ||
| 49 g/10 min @Load 2.16 kg, Temperature 260 °C | 49 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | 5mm/min; ISO 527-1, 2 | ||
| Elongation at Break | 1.7 % | 1.7 % | 5mm/min; ISO 527-1, 2 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1mm/min; ISO 527-1, 2 | ||
| Charpy Impact Unnotched | 1.30 J/cm2 | 6.19 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.160 J/cm2 | 0.761 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.2 @Frequency 1.00e+10 Hz | 2.2 @Frequency 1.00e+10 Hz | |||
| Dissipation Factor | 0.00010 @Frequency 1.00e+10 Hz | 0.00010 @Frequency 1.00e+10 Hz | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ISO 75-1, 2 | ||
| Glass Transition Temp, Tg | 140 °C | 284 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.53 | 1.53 | |||
| Transmission, Visible | 91 % | 91 % | ISO 13468-1 | ||
| Descriptive Properties | |||||
| Abbe number | 58 | ||||
| Birefringence, nm | max 20 | ||||
| Optical Stress Constant, Pa-1 | from -7E-12 to -2E-12 | ||||
| Pencil Hardness | F | JIS K5401 | |||
| Resistance to Acids | Usable | ||||
| Resistance to Alcohols | Usable | ||||
| Resistance to Alkalis | Usable | ||||
| Resistance to Aromatic Solvents | Not Usable | ||||
| Resistance to Chlorinated Solvents | Not Usable | ||||
| Resistance to Esters | Usable | ||||
| Resistance to Gasoline | Not Usable | ||||
| Resistance to Ketones | Usable | ||||
| Resistance to Oils | Not Usable | ||||