- 熔體流動速率 [g/10min]: 2.7
- 密度 [g/cm3]: 0.94
- 脆化溫度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Permeability | 4240 cm3 mil/(m2 day atm) @Temperature 23.0 °C | 274 cm3 mil/(100 in2 day atm) @Temperature 73.4 °F | 50% RH; ISO 15105-2 |
| Water Vapor Permeability | 18.4 g mil/ (m2 day) @Temperature 38.0 °C | 1.19 g mil/ (100 in2 day) @Temperature 100 °F | 90% RH; ISO 15106-3 |
| Density | 0.940 g/cc | 0.0340 lb/in3 | ISO 1183 |
| Thickness | 127 microns | 5.00 mil | |
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 11 g/10 min @Load 2.16 kg, Temperature 260 °C | 11 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 50.4 MPa @Thickness 0.0500 mm | 7310 psi @Thickness 0.00197 in | TD, Break; ASTM D882 |
| 50.6 MPa @Thickness 0.125 mm | 7340 psi @Thickness 0.00492 in | TD, Break; ASTM D882 | |
| 52.0 MPa @Thickness 0.125 mm | 7540 psi @Thickness 0.00492 in | MD, Break; ASTM D882 | |
| 60.7 MPa @Thickness 0.0500 mm | 8800 psi @Thickness 0.00197 in | MD, Break; ASTM D882 | |
| Film Elongation at Break, MD | 640 % @Thickness 0.0500 mm | 640 % @Thickness 0.00197 in | ASTM D882 |
| 800 % @Thickness 0.125 mm | 800 % @Thickness 0.00492 in | ASTM D882 | |
| Film Elongation at Break, TD | 620 % @Thickness 0.0500 mm | 620 % @Thickness 0.00197 in | ASTM D882 |
| 790 % @Thickness 0.125 mm | 790 % @Thickness 0.00492 in | ASTM D882 | |
| Tensile Modulus | 0.0340 GPa @Thickness 0.0500 mm | 4.93 ksi @Thickness 0.00197 in | TD; ASTM D882 |
| 0.0363 GPa @Thickness 0.0500 mm | 5.26 ksi @Thickness 0.00197 in | MD; ASTM D882 | |
| 0.0501 GPa @Thickness 0.125 mm | 7.26 ksi @Thickness 0.00492 in | MD; ASTM D882 | |
| 0.0527 GPa @Thickness 0.125 mm | 7.65 ksi @Thickness 0.00492 in | TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 1103 g @Load 3.20 kg, Thickness 0.0500 mm | 1103 g @Load 7.06 lb, Thickness 0.00197 in | ASTM D1922 |
| 2718 g @Load 0.00326 kg, Thickness 3.17 mm | 2718 g @Load 0.00704 lb, Thickness 0.125 in | ASTM D1922 | |
| Elmendorf Tear Strength TD | 1221 g @Load 3.20 kg, Thickness 0.0500 mm | 1221 g @Load 7.06 lb, Thickness 0.00197 in | ASTM D1922 |
| 3171 g @Load 0.00326 kg, Thickness 0.125 mm | 3171 g @Load 0.00704 lb, Thickness 0.00492 in | ASTM D1922 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.24 @Frequency 1.00e+9 Hz | 2.24 @Frequency 1.00e+9 Hz | ASTM D2520B |
| Dielectric Strength | 157 kV/mm | 4000 kV/in | ASTM D149-97a |
| Dissipation Factor | 0.00026 @Frequency 1.00e+9 Hz | 0.00026 @Frequency 1.00e+9 Hz | ASTM D2520B |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 64.0 °C | 147 °F | VST/A50; ISO 306 |
| Brittleness Temperature | <= 90.0 °C | <= 194 °F | ISO 974 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.27 % @Thickness 0.125 mm | 1.27 % @Thickness 0.00492 in | ASTM D1003 |
| 1.5 % @Thickness 0.0500 mm | 1.5 % @Thickness 0.00197 in | ASTM D1003 | |
| Gloss | 94 % @Thickness 0.0500 mm | 94 % @Thickness 0.00197 in | 60°; ASTM D2457 |
| 116 % @Thickness 0.125 mm | 116 % @Thickness 0.00492 in | 60°; ASTM D2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 84.0 °C | 183 °F | Internal Method |