- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.01
- 熱變形溫度 [℃]: 130.0
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C | 0.010 % @Temperature 73.4 °F | ISO 62 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 260 °C | 12 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 63.0 MPa | 9140 psi | Break, (5mm/min); ISO 527-2,-1A |
| Elongation at Yield | 2.6 % | 2.6 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.90 GPa | 421 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 1.40 J/cm2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.170 J/cm2 @Temperature 23.0 °C | 0.809 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1,-2 |
| Glass Transition Temp, Tg | 142 °C | 288 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |