- 熔體流動速率 [g/10min]: 9.0
- 缺口沖擊強度: 0.108
- 拉伸強度 [MPa]: 32.001
- 彎曲模量 [MPa]: 2.80
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | |
| Water Absorption | <= 0.010 % | <= 0.010 % | |
| Melt Flow | 9.0 - 14 g/10 min @Load 2.16 kg, Temperature 280 °C | 9.0 - 14 g/10 min @Load 4.76 lb, Temperature 536 °F | Z-011A |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.001 MPa | 4641.3 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| Tensile Modulus | 1.80 GPa | 261 ksi | |
| Flexural Strength | 66.0 MPa | 9570 psi | |
| Flexural Modulus | 2.80 GPa | 406 ksi | |
| Izod Impact, Notched | 0.108 J/cm | 0.202 ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 123 °C | 253 °F | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.509 | 1.509 | |
| Transmission, Visible | 92 % | 92 % | |