- 熔體流動速率 [g/10min]: 29.4
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.01
- 拉伸強度 [MPa]: 63.0
- 熱變形溫度 [℃]: 75.0
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C | 0.010 % @Temperature 73.4 °F | ISO 62 |
| Melt Flow | 29.4 g/10 min @Load 2.16 kg, Temperature 260 °C | 29.4 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.260 J/cm2 @Temperature 23.0 °C | 1.24 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.35 @Frequency 1000 - 10000 Hz | 2.35 @Frequency 1000 - 10000 Hz | IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 80.0 °C | 176 °F | B50 (50°C/h 50N); ISO 306 |
| Glass Transition Temp, Tg | 78.0 °C | 172 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | <= 60.0 °C | <= 140 °F | |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | |
| Zone 1 | 190 - 220 °C | 374 - 428 °F | |
| Zone 2 | 200 - 230 °C | 392 - 446 °F | |
| Zone 3 | 210 - 240 °C | 410 - 464 °F | |
| Zone 4 | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Injection Velocity | 50.0 - 150 mm/sec | 1.97 - 5.91 in/sec | Moderate to Fast |
| Injection Pressure | 50.0 - 110 MPa | 7250 - 16000 psi | Specific |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | Specific |
| Back Pressure | <= 15.0 MPa | <= 2180 psi | Specific |
| Screw Speed | 50 - 200 rpm | 50 - 200 rpm | |