- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 30.0
- 彎曲強度 [MPa]: 160.0
- 彎曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.00 cm/cm | 0.00 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | IEC 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Compressive Strength | 82.0 MPa | 11900 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 11.0 GPa | 1600 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 93 |
| Dielectric Constant | 3.1 @Frequency 1e+7 Hz | 3.1 @Frequency 1e+7 Hz | |
| 3.4 @Frequency 1000 Hz | 3.4 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.010 @Frequency 1e+7 Hz | 0.010 @Frequency 1e+7 Hz | |
| 0.030 @Frequency 1000 Hz | 0.030 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 135 sec | 135 sec | |
| Comparative Tracking Index | 150 V | 150 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -3.00 μm/m-°C @Temperature -50.0 - 200 °C | -1.67 μin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| -3.00 μm/m-°C @Temperature -58.0 - 390 °C | -1.67 μin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 66.0 μm/m-°C @Temperature -50.0 - 200 °C | 36.7 μin/in-°F @Temperature -58.0 - 392 °F | |
| 66.0 μm/m-°C @Temperature -50.0 - 200 °C | 36.7 μin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 325 °C | 617 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/A |
| UL RTI, Electrical | 240 °C | 464 °F | |
| UL RTI, Mechanical with Impact | 220 °C | 428 °F | |
| Flammability, UL94 | V-0 | V-0 | |