- 缺口沖擊強度: 50.5
- 彎曲模量 [MPa]: 11.13
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.099 GPa | 1609.8 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 175 MPa | 25400 psi | ISO 178 |
| Flexural Modulus | 11.13 GPa | 1614 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 50.5 kJ/m2 | 24.0 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.6 kJ/m2 @Temperature 23.0 °C | 26.9 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 3.00 μm/m-°C | 1.67 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 69.0 μm/m-°C | 38.3 μin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 150 °C | 104 - 302 °F | cavity |
| Melt Temperature | 330 - 350 °C | 626 - 662 °F | |
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 3 hour | 3 hour | |
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum |