- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 5.0
- 彎曲模量 [MPa]: 10.6
- 熱變形溫度 [℃]: 270.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.0200 % | 0.0200 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00380 cm/cm | 0.00380 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 44.0 | 44.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.00 % | 3.00 % | 50mm/min; ISO 527-2/1A | ||
| 3.10 % | 3.10 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 | ||
| Flexural Modulus | 10.6 GPa | 1540 ksi | ISO 178 | ||
| Compressive Strength | 53.0 MPa | 7690 psi | 1% strain; ISO 604 | ||
| Compressive Modulus | 7.70 GPa | 1120 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | ISO 180/1U | ||
| Charpy Impact Unnotched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.90 @Frequency 1.00e+6 Hz | 3.90 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 59.0 kV/mm | 1500 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00350 @Frequency 1.00e+6 Hz | 0.00350 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 10.0 μm/m-°C | 5.56 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 43.0 μm/m-°C | 23.9 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 185 °C | 365 °F | B50 (50°C/h 50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 130 °C | 176 - 266 °F | Cavity temperature | ||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 3 | 330 - 350 °C | 626 - 662 °F | |||
| Zone 4 | 335 - 355 °C | 635 - 671 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Screw Speed | 100 rpm @Diameter 40.0 mm | 100 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Descriptive Properties | |||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||