- 熔體流動(dòng)速率 [g/10min]: 38.0
- 密度 [g/cm3]: 0.886
- 缺口沖擊強(qiáng)度: 0.2
- 拉伸強(qiáng)度 [MPa]: 34.0
- 彎曲模量 [MPa]: 1.45
- 硬度: 79.0
- 熱變形溫度 [℃]: 99.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 | ||
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 | ||
| Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C | 38 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 79 - 108 | 79 - 108 | Normal range for injection molding resins; ASTM D785 | ||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 | ||
| Elongation at Break | 20 % | 20 % | ASTM D638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 | ||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790A | ||
| Izod Impact, Notched | 0.200 - 0.300 J/cm @Diameter 3.17 mm | 0.375 - 0.562 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Process | Fiber Spinning | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.