- 熔體流動速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.886
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 34.0
- 彎曲模量 [MPa]: 1.38
- 硬度: 79.0
- 熱變形溫度 [℃]: 99.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C | 35 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 79 - 108 | 79 - 108 | Normal range for injection molding resins; ASTM D785 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790A |
| Izod Impact, Notched | 0.200 - 0.300 J/cm @Diameter 3.17 mm | 0.375 - 0.562 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | UL Relative Thermal Index |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |