- 熔體流動速率 [g/10min]: 4.7
- 密度 [g/cm3]: 0.886
- 缺口沖擊強度: 0.2
- 拉伸強度 [MPa]: 36.0
- 彎曲模量 [MPa]: 1.48
- 硬度: 79.0
- 熱變形溫度 [℃]: 102.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 | ||
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 | ||
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.7 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 79 - 108 | 79 - 108 | Normal range for injection molding resins; ASTM D785 | ||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 | ||
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 | ||
| Flexural Modulus | 1.48 GPa | 215 ksi | ASTM D790A | ||
| Izod Impact, Notched | 0.200 - 0.300 J/cm @Diameter 3.17 mm | 0.375 - 0.562 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | UL Relative Thermal Index | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| Injection Molding | |||||
| region | Mexico | ||||
| US & Canada | |||||