- 熔體流動(dòng)速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.886
- 缺口沖擊強(qiáng)度: 0.32
- 拉伸強(qiáng)度 [MPa]: 43.0
- 彎曲模量 [MPa]: 2.14
- 硬度: 108.0
- 熱變形溫度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790A |
| Izod Impact, Notched | 0.320 J/cm @Diameter 3.17 mm | 0.599 ft-lb/in @Diameter 0.125 in | bar |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 125 °C | 257 °F | UL Relative Thermal Index |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |