- 熔體流動速率 [g/10min]: 350.0
- 密度 [g/cm3]: 0.905
- 缺口沖擊強度: 1.6
- 拉伸強度 [MPa]: 33.0
- 彎曲模量 [MPa]: 1.45
- 熱變形溫度 [℃]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Melt Flow | 350 g/10 min @Load 2.16 kg, Temperature 230 °C | 350 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 72.0 MPa | 10400 psi | 132 N/10s; ISO 2039 | ||
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 6.0 % | 6.0 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.55 GPa | 225 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 43.0 MPa | 6240 psi | |||
| Flexural Modulus | 1.45 GPa | 210 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 1.60 kJ/m2 @Temperature -20.0 °C | 0.761 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 1.80 kJ/m2 @Temperature 23.0 °C | 0.857 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 1.10 J/cm2 | 5.23 ft-lb/in2 | ISO 179/1eA | ||
| 4.50 J/cm2 | 21.4 ft-lb/in2 | ISO 179/1eA | |||
| Charpy Impact, Notched | 0.0800 J/cm2 @Temperature -30.0 °C | 0.381 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.0900 J/cm2 @Temperature -20.0 °C | 0.428 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| 0.100 J/cm2 @Temperature 23.0 °C | 0.476 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 106 μm/m-°C | 58.9 μin/in-°F | -30°C/80°C; Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 | ||
| Vicat Softening Point | 89.0 °C @Load 5.10 kg | 192 °F @Load 11.2 lb | ISO 306 | ||
| 151 °C @Load 1.02 kg | 304 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 - 260 °C | 392 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||