- 熔體流動速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 34.0
- 硬度: 102.0
- 熱變形溫度 [℃]: 94.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.600 g/cc | 0.0181 - 0.0217 lb/in3 | |||
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | mold average; Borealis Method | ||
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C | 21 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 102 | 102 | ISO 2039-2 | ||
| Ball Indentation Hardness | 70.0 MPa | 10200 psi | 358 N/30 s; ISO 2039 | ||
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.50 GPa | 218 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact Unnotched | 1.50 J/cm2 @Temperature -20.0 °C | 7.14 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Charpy Impact, Notched | 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Hot Ball Pressure Test | 125 °C @Thickness 2.00 mm | 257 °F @Thickness 0.0787 in | EN 60695-10-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 | ||
| Vicat Softening Point | 90.0 °C @Load 5.10 kg | 194 °F @Load 11.2 lb | ISO 306 | ||
| 153 °C @Load 1.02 kg | 307 °F @Load 2.25 lb | ISO 306 | |||
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 120 °C | 248 °F | UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 70 % | 70 % | 2mm plaque; DIN 67530 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||