- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.91
- 拉伸強度 [MPa]: 39.0
- 硬度: 100.0
- 熱變形溫度 [℃]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ISO 2039-2 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ISO 527-2 |
| Elongation at Yield | 7.5 % | 7.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.550 J/cm2 @Temperature 23.0 °C | 2.62 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | |