- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.908
- 拉伸強度 [MPa]: 34.5
- 彎曲模量 [MPa]: 1.55
- 硬度: 100.0
- 熱變形溫度 [℃]: 88.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.908 g/cc | 0.0328 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 100 | 100 | ISO 2039-2 | ||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.55 GPa | 225 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | high | ||||