- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.12
- 缺口沖擊強度: 8.5
- 拉伸強度 [MPa]: 100.0
- 彎曲模量 [MPa]: 6.00
- 熱變形溫度 [℃]: 159.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | average process; in flow; 150x80x2mm | ||
| 0.011 cm/cm | 0.011 in/in | average process; cross flow; 150x80x2mm | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 112 MPa | 16200 psi | 358 N/30s; ISO 2039 | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527-2 | ||
| Elongation at Break | 3.3 % | 3.3 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 6.90 GPa | 1000 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 | ||
| Flexural Modulus | 6.00 GPa | 870 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.50 kJ/m2 @Temperature -20.0 °C | 4.04 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 11.0 kJ/m2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 4.90 J/cm2 @Temperature -20.0 °C | 23.3 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| 5.80 J/cm2 @Temperature 23.0 °C | 27.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature -20.0 °C | 4.28 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ISO 75-2 | ||
| Vicat Softening Point | 135 °C @Load 5.10 kg | 275 °F @Load 11.2 lb | ISO 306 | ||
| 164 °C @Load 1.02 kg | 327 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||