- 熔體流動速率 [g/10min]: 2.4
- 拉伸強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 0.850
- 熱變形溫度 [℃]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.4 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527-2 |
| Elongation at Yield | 13 % | 13 % | ISO 527-2 |
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527-2 |
| Flexural Modulus | 0.850 GPa | 123 ksi | ISO 178 |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-2 |