- 熔體流動速率 [g/10min]: 22.0
- 密度 [g/cm3]: 1.04
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | mold average; Borealis Method | ||
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C | 22 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527-2 | ||
| Elongation at Break | 300 % | 300 % | ISO 527-2 | ||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.70 GPa | 247 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature -20.0 °C | 2.38 ft-lb/in2 @Temperature -4.00 °F | ISO 180/1A | ||
| 50.0 kJ/m2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact, Notched | 0.550 J/cm2 @Temperature -20.0 °C | 2.62 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 6.00 J/cm2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 45.0 μm/m-°C | 25.0 μin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-2 | ||
| Vicat Softening Point | 120 °C @Load 1.02 kg | 248 °F @Load 2.25 lb | ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||