- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.902
- 缺口沖擊強度: 1.6
- 拉伸強度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.32
- 硬度: 102.0
- 熱變形溫度 [℃]: 75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in3 | ASTM D1505 | ||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 102 | 102 | ASTM D-785 | ||
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min (50 mm/min); ASTM D-638 | ||
| Flexural Modulus | 1.32 GPa | 191 ksi | Secant @ 1% strain; ASTM D-790 | ||
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | ASTM D-648 | ||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| Injection Molding | |||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||