- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.262
- 拉伸強度 [MPa]: 13.0
- 斷裂伸長率 [%]: 17.0
- 彎曲強度 [MPa]: 11.0
- 彎曲模量 [MPa]: 0.241
- 硬度: 44.0
- 熱變形溫度 [℃]: 53.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 - 1.45 g/cc | 0.0368 - 0.0524 lb/in3 | Average value: 1.23 g/cc Grade Count:77 |
| Filler Content | 40.0 % | 40.0 % | Average value: 40.0 % Grade Count:31 |
| Water Absorption | 0.0200 - 0.0400 % | 0.0200 - 0.0400 % | Average value: 0.0245 % Grade Count:11 |
| Linear Mold Shrinkage | 0.00700 - 0.0160 cm/cm | 0.00700 - 0.0160 in/in | Average value: 0.0104 cm/cm Grade Count:59 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0140 - 0.0150 cm/cm | 0.0140 - 0.0150 in/in | Average value: 0.0143 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0156 cm/cm | 0.00800 - 0.0156 in/in | Average value: 0.0113 cm/cm Grade Count:5 |
| Melt Flow | 1.00 - 30.0 g/10 min | 1.00 - 30.0 g/10 min | Average value: 11.4 g/10 min Grade Count:52 |
| Ash | 39.6 - 40.0 % | 39.6 - 40.0 % | Average value: 40.0 % Grade Count:15 |
| 24.0 - 63.0 % @Temperature 600 - 900 °C | 24.0 - 63.0 % @Temperature 1110 - 1650 °F | Average value: 35.3 % Grade Count:3 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 44.0 - 99.0 | 44.0 - 99.0 | Average value: 84.5 Grade Count:33 |
| Hardness, Shore D | 68.0 - 75.0 | 68.0 - 75.0 | Average value: 72.8 Grade Count:8 |
| Tensile Strength, Ultimate | 11.0 - 28.0 MPa | 1600 - 4060 psi | Average value: 20.3 MPa Grade Count:38 |
| Tensile Strength, Yield | 13.0 - 31.0 MPa | 1890 - 4500 psi | Average value: 22.2 MPa Grade Count:49 |
| Elongation at Break | 2.00 - 470 % | 2.00 - 470 % | Average value: 59.4 % Grade Count:54 |
| Elongation at Yield | 2.00 - 90.0 % | 2.00 - 90.0 % | Average value: 11.0 % Grade Count:30 |
| Modulus of Elasticity | 1.40 - 3.30 GPa | 203 - 479 ksi | Average value: 2.46 GPa Grade Count:26 |
| Flexural Yield Strength | 17.0 - 48.3 MPa | 2470 - 7000 psi | Average value: 35.1 MPa Grade Count:40 |
| Flexural Modulus | 0.241 - 3.85 GPa | 35.0 - 558 ksi | Average value: 2.17 GPa Grade Count:73 |
| Izod Impact, Notched | 0.262 - 7.74 J/cm | 0.490 - 14.5 ft-lb/in | Average value: 0.869 J/cm Grade Count:62 |
| Izod Impact, Unnotched | 3.20 - 5340 J/cm | 6.00 - 10000 ft-lb/in | Average value: 10.5 J/cm Grade Count:20 |
| 0.250 - 0.250 J/cm @Temperature 0.000 - 0.000 °C | 0.468 - 0.468 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.250 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 2.80 - 45.0 kJ/m2 | 1.33 - 21.4 ft-lb/in2 | Average value: 10.6 kJ/m2 Grade Count:8 |
| 2.00 - 3.70 kJ/m2 @Temperature -30.0 - -20.0 °C | 0.952 - 1.76 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 2.45 kJ/m2 Grade Count:4 | |
| Charpy Impact Unnotched | 5.00 - 1000 J/cm2 | 23.8 - 4760 ft-lb/in2 | Average value: 5.50 J/cm2 Grade Count:3 |
| 1.40 - 2.00 J/cm2 @Temperature -40.0 - -20.0 °C | 6.66 - 9.52 ft-lb/in2 @Temperature -40.0 - -4.00 °F | Average value: 1.85 J/cm2 Grade Count:4 | |
| Charpy Impact, Notched | 0.300 - 0.350 J/cm2 | 1.43 - 1.67 ft-lb/in2 | Average value: 0.338 J/cm2 Grade Count:4 |
| 0.100 - 0.100 J/cm2 @Temperature -20.0 - -20.0 °C | 0.476 - 0.476 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 0.100 J/cm2 Grade Count:1 | |
| Gardner Impact | 1.47 - 33.9 J | 1.08 - 25.0 ft-lb | Average value: 14.6 J Grade Count:21 |
| 3.62004 - 19.4334 J @Temperature -30.0 - -5.56 °C | 2.67000 - 14.3334 ft-lb @Temperature -22.0 - 22.0 °F | Average value: 8.81 J Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | Average value: 8.71e+15 ohm-cm Grade Count:7 |
| Dielectric Strength | 19.7 - 23.0 kV/mm | 500 - 584 kV/in | Average value: 20.8 kV/mm Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.4 - 63.0 μm/m-°C | 28.0 - 35.0 μin/in-°F | Average value: 55.7 μm/m-°C Grade Count:6 |
| Thermal Conductivity | 0.231 - 0.288 W/m-K | 1.60 - 2.00 BTU-in/hr-ft2-°F | Average value: 0.269 W/m-K Grade Count:3 |
| Melting Point | 150 - 182 °C | 302 - 360 °F | Average value: 164 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 53.9 - 127 °C | 129 - 260 °F | Average value: 107 °C Grade Count:57 |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.4 - 96.1 °C | 112 - 205 °F | Average value: 67.3 °C Grade Count:47 |
| Vicat Softening Point | 76.0 - 154 °C | 169 - 309 °F | Average value: 117 °C Grade Count:11 |
| Flammability, UL94 | HB | HB | Grade Count:23 |
| Optical Properties | Metric | English | Comments |
| Gloss | 45.0 - 55.0 % | 45.0 - 55.0 % | Average value: 51.3 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 227 °C | 380 - 440 °F | Average value: 210 °C Grade Count:7 |
| Nozzle Temperature | 200 - 238 °C | 392 - 460 °F | Average value: 219 °C Grade Count:6 |
| Melt Temperature | 170 - 279 °C | 338 - 534 °F | Average value: 217 °C Grade Count:16 |
| Mold Temperature | 15.6 - 70.0 °C | 60.0 - 158 °F | Average value: 48.1 °C Grade Count:21 |
| Drying Temperature | 65.6 - 100 °C | 150 - 212 °F | Average value: 79.2 °C Grade Count:10 |
| Dry Time | 1.00 - 3.00 hour | 1.00 - 3.00 hour | Average value: 1.80 hour Grade Count:10 |
| Moisture Content | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0340 % Grade Count:5 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 69.7 MPa Grade Count:14 |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | Average value: 5.17 MPa Grade Count:3 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:3 |