- 密度 [g/cm3]: 1.13
- 缺口沖擊強(qiáng)度: 0.32
- 拉伸強(qiáng)度 [MPa]: 42.0
- 彎曲模量 [MPa]: 1.41
- 熱變形溫度 [℃]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 |
| 1.14 g/cc | 0.0412 lb/in3 | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D 955 |
| 0.0082 cm/cm @Time 86400 sec | 0.0082 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0098 cm/cm @Time 86400 sec | 0.0098 in/in @Time 24.0 hour | ISO 294 |
| 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527 |
| 40.0 MPa | 5800 psi | ASTM D 638 | |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D 638 |
| 42.0 MPa | 6090 psi | ISO 527 | |
| Elongation at Break | 18.4 % | 18.4 % | ASTM D 638 |
| 20.3 % | 20.3 % | ISO 527 | |
| Elongation at Yield | 6.2 % | 6.2 % | ISO 527 |
| 6.7 % | 6.7 % | ASTM D 638 | |
| Tensile Modulus | 1.47 GPa | 213 ksi | 1 mm/min; ISO 527 |
| 1.75 GPa | 254 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| 55.0 MPa | 7980 psi | ASTM D 790 | |
| Flexural Modulus | 1.41 GPa | 205 ksi | ISO 178 |
| 1.66 GPa | 241 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C | 0.599 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 5.39 J/cm @Temperature 23.0 °C | 10.1 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 @Temperature 23.0 °C | 21.4 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J @Temperature 23.0 °C | 1.48 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+9 - 1.00e+11 ohm-cm | 1.00e+9 - 1.00e+11 ohm-cm | ASTM D 257 |
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D 257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 101 μm/m-°C @Temperature -40.0 - 40.0 °C | 56.1 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 101 μm/m-°C @Temperature -40.0 - 40.0 °C | 56.1 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 108 μm/m-°C @Temperature -40.0 - 40.0 °C | 60.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 109 μm/m-°C @Temperature -40.0 - 40.0 °C | 60.6 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 79.0 °C @Thickness 3.20 mm | 174 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 67.0 °C @Thickness 3.20 mm | 153 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |